CHỦNG LOẠI FRIT
|
Mã frit
|
Thành phần hóa (%)
|
Hệ số giản nở nhiệt
|
Điểm biến mềm
|
Nhiệt độ nung
(oC)
|
Sử dụng
|
|
SiO2
|
Al2O3
|
Na2O
|
K2O
|
CaO
|
MgO
|
BaO
|
ZnO
|
B2O3
|
ZrO2
|
P2O5
|
TiO2
|
SrO
|
COE 3*α
(10-7 K-1)
|
S.P.
(oC)
|
|
FRIT TRONG
|
FT163
|
58-61
|
5-7
|
0-2
|
3-6
|
12-15
|
1-3
|
2-4
|
7-10
|
3-5
|
|
|
|
|
228 ± 9
|
730±15
|
1055- 1095
|
W
|
|
FT167
|
60-63
|
6-8
|
0-2
|
2-4
|
14-17
|
1-3
|
1-3
|
3-5
|
4-7
|
|
|
|
|
213 ± 9
|
850±15
|
1050-1090
|
W
|
|
FT168
|
59-62
|
8-11
|
1-3
|
4-7
|
12-15
|
1-3
|
|
1-3
|
6-9
|
|
|
|
|
201 ± 9
|
740±15
|
1060- 1100
|
W
|
|
FT162
|
57-60
|
6-8
|
1-2
|
4-6
|
10-13
|
1-3
|
3-5
|
6-8
|
4-6
|
|
|
|
|
219 ± 9
|
749±15
|
1070- 1110
|
W
|
|
FT156
|
61-65
|
5-7
|
1-2
|
1-3
|
12-15
|
1-3
|
2-4
|
4-6
|
3-6
|
|
|
|
|
246 ± 9
|
900±15
|
1090-1120
|
W
|
|
FT152
|
62-65
|
5-7
|
1-3
|
2-4
|
12-15
|
1-3
|
2-4
|
5-7
|
2-4
|
|
|
|
|
192 ± 9
|
845±15
|
1080-1115
|
W
|
|
HT082
|
59-63
|
7-9
|
0-1
|
3-5
|
13-15
|
0-2
|
|
8-11
|
2-4
|
|
|
|
|
216 ± 9
|
818±15
|
1080-1125
|
W
|
|
FT157
|
60-63
|
5-7
|
0-2
|
3-6
|
13-15
|
1-3
|
1-3
|
6-8
|
2-4
|
|
|
|
|
219 ± 9
|
824±15
|
1085-1125
|
W
|
|
FT178
|
60-64
|
6-8
|
1-2
|
3-5
|
12-15
|
1-3
|
|
9-12
|
3-5
|
|
|
|
|
219 ± 9
|
775±15
|
1095-1125
|
W
|
|
FT378
|
64-66
|
4-6
|
1-2
|
1-3
|
13-15
|
1-2
|
3-4
|
3-5
|
3-5
|
|
|
|
|
225 ± 9
|
762±15
|
1100-1130
|
W
|
|
FT189
|
63-66
|
5-7
|
1-2
|
2-4
|
12-15
|
0-3
|
1-3
|
3-6
|
3-5
|
|
|
|
|
198 ± 9
|
740±15
|
1105-1135
|
W
|
|
FT246
|
65-69
|
7-9
|
0-2
|
1-3
|
14-17
|
1-3
|
0-2
|
2-4
|
1-3
|
|
|
0-2
|
|
222 ± 9
|
815±15
|
1110-1140
|
W, F
|
|
FT216
|
65-68
|
6-8
|
0-2
|
1-4
|
15-18
|
1-3
|
|
3-5
|
1-3
|
|
|
|
|
182 ± 9
|
882±15
|
1130-1165
|
F
|
|
FT259
|
65-68
|
5-8
|
0-2
|
1-3
|
15-18
|
1-3
|
|
5-8
|
|
|
|
|
|
239 ± 9
|
>950
|
1135-1165
|
W, F
|
|
FT253
|
62-65
|
6-8
|
0-2
|
0-3
|
16-19
|
1-3
|
0-2
|
6-8
|
0-3
|
|
|
|
|
234 ± 9
|
910±15
|
1135-1165
|
W, F
|
|
FT357
|
63-66
|
3-5
|
1-2
|
0-3
|
15-17
|
3-4
|
1-2
|
4-6
|
0-2
|
|
|
|
1-2
|
234 ± 9
|
823±15
|
1135-1175
|
F
|
|
FT399
|
64-66
|
6-7
|
1-3
|
1-2
|
14-17
|
2-3
|
0-1
|
5-7
|
0-1
|
|
|
|
|
216 ± 9
|
840±15
|
1135-1175
|
F
|
|
FT355
|
64-67
|
5-7
|
0-2
|
2-4
|
14-16
|
0-3
|
1-3
|
1-4
|
1-3
|
|
|
|
2-3
|
249 ± 9
|
>950
|
1140-1170
|
F
|
|
FT328
|
66-69
|
4-7
|
1-2
|
1--3
|
13-15
|
2-4
|
1-3
|
4-6
|
1-2
|
|
|
|
|
237 ± 9
|
857±15
|
1140-1175
|
F
|
|
FT369
|
65-67
|
4-6
|
0-2
|
2-4
|
16-18
|
1-4
|
0-2
|
4-6
|
1-2
|
|
|
|
3-5
|
249 ± 9
|
920±15
|
1150-1185
|
F
|
|
FT370
|
64-67
|
4-6
|
0-1
|
1-3
|
17-19
|
1-2
|
|
7-9
|
|
|
0-2
|
|
|
255 ± 9
|
920±15
|
1155-1185
|
F
|
|
FT207
|
67-71
|
5-8
|
1-3
|
1-3
|
16-19
|
0-3
|
|
|
1-3
|
|
|
|
|
198 ± 9
|
804 ± 15
|
1140-1180
|
F
|
|
FT212
|
65-70
|
5-9
|
0-2
|
1-3
|
16-20
|
1-3
|
1-3
|
|
1-3
|
|
|
|
0-1
|
174 ± 9
|
916 ± 15
|
1140-1181
|
F
|
|
FT213
|
66-69
|
6-9
|
0-2
|
1-3
|
16-20
|
1-3
|
|
|
1-3
|
|
|
|
|
192 ± 9
|
913 ± 15
|
1140-1180
|
F
|
|
FT107
|
66-70
|
6-9
|
7-9
|
0-2
|
8-11
|
2-4
|
|
|
|
|
|
|
|
222 ± 9
|
656±15
|
1100-1130
|
E
|
|
FT117
|
71-74
|
0-2
|
6-9
|
0-2
|
15-18
|
1-4
|
|
|
|
|
|
|
|
376 ± 9
|
>950
|
1130-1160
|
E
|
|
FRIT ĐỤC
|
HO037
|
52-57
|
6-9
|
1-3
|
2-4
|
8-11
|
2-4
|
|
1-3
|
6-9
|
7-9
|
|
|
|
204 ± 9
|
713±15
|
1060-1090
|
W
|
|
HO038
|
51-55
|
4-7
|
1-3
|
3-6
|
10-13
|
2-4
|
|
3-6
|
7-10
|
6-8
|
|
|
|
213 ± 9
|
744±16
|
1080-1110
|
W
|
|
HO240
|
55-58
|
1-3
|
1-2
|
2-5
|
5-7
|
1-3
|
|
12-14
|
4-5
|
6-9
|
0-2
|
|
|
195 ± 9
|
774±15
|
1090-1120
|
W
|
|
HO062
|
57-60
|
4-6
|
1-3
|
3-4
|
8-10
|
2-4
|
|
10-13
|
0-3
|
7-8
|
1-3
|
|
|
198 ± 9
|
790±15
|
1125-1155
|
W, F
|
|
FRIT BÁN ĐỤC
|
FS462
|
60-63
|
3-5
|
0-2
|
4-6
|
12-14
|
1-3
|
|
6-8
|
4-6
|
|
0-2
|
|
|
213 ± 9
|
763±15
|
1070-1110
|
W
|
|
FS459
|
60-63
|
3-5
|
0-2
|
4-6
|
10-14
|
2-4
|
|
7-10
|
3-5
|
1-3
|
0-2
|
|
|
212 ± 9
|
794±15
|
1085-1115
|
W
|
|
FS456
|
63-66
|
2-5
|
1-2
|
4-6
|
10-12
|
2-4
|
|
5-7
|
3-5
|
|
|
|
|
213 ± 9
|
763±15
|
1090-1130
|
W, F
|
|
FRIT MỜ
|
HM007
|
52-55
|
10-13
|
0-2
|
4-6
|
9-12
|
0-2
|
8-10
|
6-8
|
1-3
|
|
|
|
|
219 ± 9
|
-
|
1130-1160
|
W, F
|
|
HP427
|
47-50
|
14-17
|
2-3
|
2-4
|
18-21
|
2-4
|
1-3
|
6-8
|
|
|
|
|
|
216 ± 9
|
>950
|
1160-1220
|
F
|
|
HP428
|
53-56
|
16-18
|
3-5
|
0-2
|
17-19
|
0-2
|
|
4-6
|
|
|
|
|
|
195 ± 9
|
>1000
|
1160-1220
|
F
|
|
FRIT ĐỤC ĐIỀU CHỈNH
|
FO126
|
45-49
|
12-15
|
9-11
|
5-7
|
7-9
|
5-7
|
|
|
1-3
|
8-10
|
|
|
|
312 ± 9
|
628±15
|
1090-1120
|
E
|
|
FO128
|
49-53
|
8-11
|
7-11
|
4-7
|
7-11
|
4-7
|
|
|
1-3
|
8-12
|
0-1
|
|
|
315 ± 9
|
-
|
1100-1130
|
E
|
|
HO109
|
44-47
|
14-17
|
4-6
|
7-9
|
8-10
|
7-9
|
|
0-3
|
|
6-8
|
|
|
|
294 ± 9
|
961±15
|
1150-1180
|
E
|
|
FRIT TITAN COE TB
|
FO102
|
62-65
|
4-6
|
2-4
|
0-2
|
12-14
|
0-2
|
|
|
2-4
|
|
|
10-12
|
|
222 ± 9
|
812±15
|
1090-1120
|
E
|
|
FO105
|
62-65
|
6-8
|
1-3
|
4-6
|
11-14
|
0-2
|
|
|
1-3
|
|
|
7-9
|
|
204 ± 9
|
820 ± 15
|
1095-1125
|
E
|
|
FO130
|
62-66
|
5-7
|
1-3
|
1-3
|
16-20
|
1-3
|
|
|
|
|
|
6-8
|
|
210 ± 9
|
>950
|
1170-1200
|
E
|
|
FO223
|
62-67
|
6-9
|
1-3
|
3-5
|
13-16
|
1-3
|
|
|
0-3
|
|
|
6-8
|
|
168 ± 9
|
|
1085-1110
|
E
|
|
FRIT TITAN COE CAO
|
FO113
|
52-55
|
5-7
|
3-5
|
3-4
|
18-21
|
1-3
|
|
|
|
|
|
11-13
|
|
276 ± 9
|
>950
|
1160-1190
|
E
|
|
FRIT TITAN ĐIỀU CHỈNH
|
FO118
|
48-51
|
11-13
|
5-7
|
7-9
|
12-15
|
0-2
|
|
|
|
|
|
11-13
|
|
300 ± 9
|
674± 15
|
1090-1120
|
E
|
Lưu ý: Kết quả trên chỉ mang tính tham khảo, tùy thuộc vào điều kiện thí nghiệm.
F: Gạch Lát
W: Gạch Ốp
E: Engobe
|