Trang chủ » Catalogue » Chỉ tiêu lý hoá Frit

Chỉ tiêu lý hoá Frit

                                                                                                                                                   240606

CHỦNG LOẠI FRIT Mã frit  Thành phần hóa (%)  Hệ số giản nở nhiệt Điểm biến mềm Nhiệt độ nung
(oC)		 Sử dụng
SiO2 Al2O3 Na2O K2O CaO MgO BaO ZnO B2O3 ZrO2 P2O5 TiO2 SrO COE 3*α
(10-7 K-1)		 S.P.
(oC)
FRIT TRONG FT167 60-63 6-8 0-2 2-4 14-17 1-3 1-3 3-5 4-7         213 ± 9 850±15 1050-1090  W 
FT163 58-61 5-7 0-2 3-6 12-15 1-3 2-4 7-10 3-5         228 ± 9 730±15 1055- 1095  W 
FT168 59-62 8-11 1-3 4-7 12-15 1-3   1-3 6-9         201 ± 9 740±15 1060- 1100  W 
FT162 57-60 6-8 1-2 4-6 10-13 1-3 3-5 6-8 4-6         219 ± 9 749±15 1070- 1110  W 
FT156 61-65 5-7 1-2 1-3 12-15 1-3 2-4 4-6 3-6         246 ± 9 900±15 1090-1120  W 
HT082 59-63 7-9 0-1 3-5 13-15 0-2   8-11 2-4         216 ± 9 818±15 1080-1125  W 
FT157 60-63 5-7 0-2 3-6 13-15 1-3 1-3 6-8 2-4         219 ± 9 824±15 1085-1125  W 
FT178 60-64 6-8 1-2 3-5 12-15 1-3   9-12 3-5         219 ± 9 775±15 1095-1125  W 
FT378 64-66 4-6 1-2 1-3 13-15 1-2 3-4 3-5 3-5         225 ± 9 762±15 1100-1130  W 
FT189 63-66 5-7 1-2 2-4 12-15 0-3 1-3 3-6 3-5         198 ± 9 740±15 1105-1135  W 
FT246 65-69 7-9 0-2 1-3 14-17 1-3 0-2 2-4 1-3     0-2   222 ± 9 815±15 1110-1140  W, F 
FT242 65-67 6-8 0-2 2-4 14-16 2-3 1-2 1-3 2-3       0-1 180 ± 9 825±15 1115-1145  W, F 
FT253 62-65 6-8 0-2 0-3 16-19 1-3 0-2 6-8 0-3         234 ± 9 910±15 1135-1165  W, F 
FT259 65-68 5-8 0-2 1-3 15-18 1-3   5-8           239 ± 9 >950 1135-1165  W, F 
FT357 63-66 3-5 1-2 0-3 15-17 3-4 1-2 4-6 0-2       1-2 234 ± 9 823±15 1135-1175   F 
FT399 64-66 6-7 1-3 1-2 14-17 2-3 0-1 5-7 0-1         216 ± 9 840±15 1135-1175  F 
FT355 64-67 5-7 0-2 2-4 14-16 0-3 1-3 1-4 1-3       2-3 249 ± 9 >950 1140-1170   F 
FT328 66-69 4-7 1-2 1--3 13-15 2-4 1-3 4-6 1-2         237 ± 9 857±15 1140-1175  F 
FT369 65-67 4-6 0-2 2-4 16-18 1-4 0-2 4-6 1-2       3-5 249 ± 9 920±15 1150-1185  F 
FT370 64-67 4-6 0-1 1-3 17-19 1-2   7-9     0-2     255 ± 9 920±15 1155-1185  F 
FT218 65-68 8-10 1-3 3-5 13-16 1-3 0-2   2-4       0-2 174 ± 9 761 ± 15 1135-1165  F 
FT207 67-71 5-8 1-3 1-3 16-19 0-3     1-3         198 ± 9 804 ± 15 1140-1180  F 
FT208 65-69 5-8 1-3 1-3 16-19 0-3 1-3   1-3         225 ± 9 912 ± 15 1140-1180  F 
FT209 65-70 5-9 0-2 1-3 16-20 1-3 1-3   1-3       0-1 195 ± 9 827 ± 15 1140-1181  F 
FT107 66-70 6-9 7-9 0-2 8-11 2-4               222 ± 9 656±15 1100-1130 E
FRIT ĐỤC HO037 52-57 6-9 1-3 2-4 8-11 2-4   1-3 6-9 7-9       204 ± 9 713±15 1060-1090   W 
HO038 51-55 4-7 1-3 3-6 10-13 2-4   3-6 7-10 6-8       213 ± 9 744±16 1080-1110   W 
HO240 55-58 1-3 1-2 2-5 5-7 1-3   12-14 4-5 6-9 0-2     195 ± 9 774±15 1090-1120  W 
HO062 57-60 4-6 1-3 3-4 8-10 2-4   10-13 0-3 7-8 1-3     198 ± 9 790±15 1125-1155  W, F 
FRIT BÁN ĐỤC FS462 60-63 3-5 0-2 4-6 12-14 1-3   6-8 4-6   0-2     213 ± 9 763±15 1070-1110  W 
FS459 60-63 3-5 0-2 4-6 10-14 2-4   7-10 3-5 1-3 0-2     212 ± 9 794±15 1085-1115   W 
FS456 63-66 2-5 1-2 4-6 10-12 2-4   5-7 3-5         213 ± 9 763±15 1090-1130   W, F 
FRIT MỜ HM007 52-55 10-13 0-2 4-6 9-12 0-2 8-10 6-8 1-3         219 ± 9 - 1130-1160  W, F 
HM002 52-54 8-10 0-2 2-4 7-9 1-2 10-13 13-15           159 ± 9 - 1125-1165  W, F 
HP427 47-50 14-17 2-3 2-4 18-21 2-4 1-3 6-8           216 ± 9 >950 1160-1220  F 
FRIT ĐỤC ĐIỀU CHỈNH FO126 45-49 12-15 9-11 5-7 7-9 5-7     1-3 8-10       312 ± 9 628±15 1090-1120  E 
FO128 49-53 8-11 7-11 4-7 7-11 4-7     1-3 8-12 0-1     315 ± 9   1100-1130  E 
HO109 44-47 14-17 4-6 7-9 8-10 7-9   0-3   6-8       294 ± 9 961±991 1150-1180 E
FRIT TITAN COE TB FO102 62-65 4-6 2-4 0-2 12-14 0-2     2-4     10-12   222 ± 9 812±15 1090-1120  E 
FO105 62-65 6-8 1-3 4-6 11-14 0-2     1-3     7-9   204 ± 9 820 ± 15 1095-1125  E 
FO130 62-66 5-7 1-3 1-3 16-20 1-3           6-8   164 ± 9 >950 1170-1200  E 
FRIT TITAN COE CAO FO113 52-55 5-7 3-5 3-4 18-21 1-3           11-13   276 ± 9 >950 1160-1190  E 
FRIT TITAN ĐIỀU CHỈNH FO118 48-51 11-13 5-7 7-9 12-15 0-2           11-13   300 ± 9 800± 15 1090-1120  E 

Lưu ý: Kết quả trên chỉ mang tính tham khảo, tùy thuộc vào điều kiện thí nghiệm

 

Ghi chú:

F: Gạch lát nền                     COE: Hệ số giãn nở nhiệt 3*α

W: Gạch ốp tường                S.P: Điểm biến mềm

E: Engobe                             

 

 

 
   In trang